Paredes Aguilar, LuisCrespin Sanchez, CinthyaSlee del Aguila, Maria Marisol2022-03-112022-03-112021-12-15http://hdl.handle.net/20.500.14503/1717El presente trabajo de investigación tiene como principal objetivo determinar la variación de la fluidez y la resistencia a la compresión del concreto simple, f’c = 210 kg/cm2, al sustituir parcialmente el cemento portland tipo I por partículas de nanosilice, para mejorar su resistencia a la compresión, y buscando así la reducción de costos en la elaboración del concreto f’c = 210 kg/cm2. La presente es una investigación experimental desarrollada teniendo en consideración y cumplimiento de las normas técnicas del Concreto ASTM, MTC, ACI y NTP. Se realizaron ensayos de los agregados a utilizar (granulometría, humedad natural, peso específico, peso unitario, abrasión) para el diseño de concreto f’c = 210 kg/cm2 verificando que estás cumplan con los parámetros de la normas técnicas peruana E.060 para concreto armada, un primer diseño denominado “diseño patrón” sin adición del nanosilice, posterior a esto se procedió a realizar mezclas con la adición del 1%, 3% y 5% de nanosilice que sustituyo parcialmente al cemento, todos los diseños se realizaron según norma ACI-211, una vez concluidos los diseños se moldeo los testigos de concreto para la realización del ensayo a la comprensión axial, en la prensa, comparando los resultado obtenidos en cada uno los diseños de mezcla de concreto, asimismo se tomó la prueba de Slump para verificar la variación de esta en los 4 diseños antes mencionados, para los registros del resultados se utilizado como instrumento una ficha técnica de recolección de datos. Se determinó finalmente que la adición de partículas de nanosilice mejoran la resistencia a la comprensión del concreto simple y la trabajabilidad de este.The main objective of this research study is to determine the variation of fluidity and compressive strength of simple concrete, f'c = 210 kg / cm2, by partially replacing type I portland cement with nanosilice particles, to improve its resistance to compression, and thus seeking to reduce overall costs. We carry out an experimental investigation using the technical standards of Concrete ASTM, MTC, ACI and NTP, complying with the physical and mechanical characteristics that they stipulate. Tests of the aggregates to be used (granulometry, natural humidity, specific weight, unit weight, abrasion) were carried out for the concrete design f'c = 210 kg / cm2 verifying that they comply with the parameters of the Peruvian technical standards E.060 For reinforced concrete, a first design called "pattern design" without adding the nanosilice, after this we proceeded to make mixtures with the addition of 1%, 3% and 5% of nanosilice that partially replaced the cement, all designs were made According to the ACI-211 standard, once the designs were completed, the concrete cores were molded to carry out the axial compression test, in the press, comparing the results obtained in each one of the concrete mix designs, the test was also taken of slump to verify the variation of this in the 4 aforementioned designs, for the records of the results a technical data collection sheet was used as an instrument. It was finally determined that the addition of nanosilize particles improves the resistance to compression of simple concrete and its workability.application/pdfspainfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/3.0/us/NanosiliceResistenciaResistencia a la compresiónConcreto simpleNanosiliceStrengthCompressive strengthSimple concreteinfo:eu-repo/semantics/bachelorThesishttps://purl.org/pe-repo/ocde/ford#2.01.00