Cabanillas Oliva, Erlin GuillermoReyes Villanueva, José GabrielTrigoso Arteaga, Nardy Isabel2025-03-242024-12-19http://hdl.handle.net/20.500.14503/3240La presente investigación de tesis aborda la influencia del aditivo CHEMA PLAST 120D, en las propiedades físicas y mecánicas del concreto cemento – arena elaborado con relaciones A/C de 0.56, 0.58 y 0.60, de resistencia a la compresión entre 315 kg/cm2 y 350kg/cm2. Es una investigación tipo cuantitativa de nivel descriptivo explicativo, de diseño cuasi experimental, con 132 probetas entre concreto patrón y experimental, correspondiendo 33 al concreto patrón (24 para compresión y 9 para flexion) y 99 al concreto experimental ( 72 para compresión y 27 para flexion). Las muestras para el concreto experimental se obtuvo adicionando al concreto patrón, dosificaciones de 15kg/m3, 20kg/m3 y 25kg/m3 de fibras. La verificación de resistencia a la compresión se realizó a los 7 y 28 dias y la resistencia a la flexion a los 28 dias de curado. Como resultados se determinó que la adicion de estas fibras incluye en las propiedades físicas y mecánicas del concreto cemento – arena; asi el peso unitario se incrementa, pero el slump al igual que el contenido de aire disminuye según se incrementa la dosificación de fibra. La resistencia a la compresión del concreto patrón más alta correspondió a la relación A/C= 0.,56 cuyo valor de 340 kg/cm2 vario hasta 394 kg/cm2 correspondiendo a la dosificación de 20 kg/cm2 de fibra den acero; y para la resistencia a la flexión el mayor valor se obtuvo para la relación A/C= 0.58, cuyo valor de 46kg/cm2 subió a 47 kg/cm2 para la misma dosificación de 20 kg/ cm3 de fibra. Asimismo, se observa que para dosificaciones de fibra de acero menores o iguales a 20kg/cm2 tanto los valores de resistencia a la compresión como de resistencia a la flexión subieron, y para la dosificación de 25 kg/m3 de fibra estos valores, para ambos tipos de resistencia bajaron, a excepción de la resistencia de la dosificación A/C= 0.56, en que mantuvieron próximas a las resistencias del concreto patrón, confirmándose la hipótesis general.This thesis research addresses the influence of CHEMA PLAST 120D additive on the physical and mechanical properties of cement-sand concrete prepared with A/C ratios of 0.56, 0.58 and 0.60, with a compressive strength between 315 kg/cm2 and 350 kg/cm2. It is a quantitative, descriptive and explanatory research, with a quasi-experimental design, with 132 test specimens between standard and experimental concrete, of which 33 were standard concrete (24 for compression and 9 for flexure) and 99 were experimental concrete (72 for compression and 27 for flexure). The samples for the experimental concrete were obtained by adding fibers of 15 kg/m3, 20 kg/m3 and 25 kg/m3 to the standard concrete. The compressive strength was verified at 7 and 28 days, and the flexural strength at 28 days of curing. As a result, it was determined that the addition of these fibers affects the physical and mechanical properties of cement-sand concrete; thus, the unit weight increases, but the slump as well as the air content decreases as the fiber dosage increases. The highest compressive strength of the standard concrete corresponded to the ratio A/C= 0.56, whose value of 340 kg/cm2 varied up to 394 kg/cm2 corresponding to the dosage of 20 kg/cm2 of steel fiber; and for the flexural strength, the highest value was obtained for the ratio A/C= 0.58, whose value of 46 kg/cm2 rose to 47 kg/cm2 for the same dosage of 20 kg/cm3 of fiber. Likewise, it is observed that for steel fiber dosages less than or equal to 20 kg/cm2, both the compressive strength and flexural strength values increased, and for the dosage of 25 kg/m3 of fiber, these values, for both types of resistance, decreased, except for the resistance of the dosage A/C= 0.56, in which they remained close to the resistances of the standard concrete, confirming the general hypothesis.application/pdfspainfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/3.0/us/Concreto cemento – arenaFibras wirand FF3CompresiónFlexiónCement-sand concreteWirand FF3 fibersCompressionBendingInfluencia del aditivo chema plast 120 d en las propiedades fisicas y mecanicas del concreto cemento-arena, elaborado con agregado de cantera km 25+500 carretera Iquitos Nauta, Iquitos- 2024info:eu-repo/semantics/bachelorThesishttps://purl.org/pe-repo/ocde/ford#2.01.00