Influencia del aditivo polifuncional sikament 290 n, en las propiedades en estado fresco y endurecido del concreto cemento – arena, Iquitos – 2024
dc.contributor.advisor | Irigoin Cabrera, Octavio Ulises | |
dc.contributor.author | Ramírez Enciso, Blanca Flor | |
dc.contributor.author | Ríos García, Willi | |
dc.date.accessioned | 2025-10-02T15:57:47Z | |
dc.date.issued | 2025-07-16 | |
dc.description.abstract | En esta tesis se investigó la influencia del aditivo polifuncional Sikament 290 N, en las propiedades físicas y mecánicas del concreto cemento – arena de resistencia a la compresión entre 245 kg/cm2 y 385 kg/cm2, elaborada con arena de 1.98 de módulo de fineza, cemento Portland Tipo I marca Cemento Amazónico Tipo GU; con relaciones A/C de 0.45, 0.55 y 0.65. Es una investigación tipo cuantitativa de nivel descriptivo explicativo, de diseño cuasi experimental, con 693 probetas entre concreto patrón y experimental, correspondiendo 99 al concreto patrón (72 para compresión y 27 para flexión) y 594 al experimental (432 para compresión y 162 para flexión). Las muestras para el experimento, en dosificación Sikament 290 N plastificante se obtuvieron adicionando al concreto patrón, dosificaciones de 0.3%, 0.5% y 0.7% y en dosificación superplastificante adicionando 0.71%, 1.06% y 1.42%. La resistencia a la compresión se evaluó a los 3, 7 y 28 días y la flexión a los 28 días de curado. La adición de Sikament 290 N, en el rango de dosificaciones de plastificante y superplastificante sí influye en las propiedades en estado fresco de asentamiento, aire atrapado, peso unitario; y, estado endurecido de resistencia a la compresión y resistencia a la flexión; aunque, en su dosificación para actuar como plastificante no es rentable, dado que en la relación óptima A/C= 0.65 y dosificación 0.5% se usaría adicionalmente 0.01 bolsas de cemento y la adición de 6.46 kg de aditivo, por cada m3 de mezcla y la mejora de resistencia a la compresión y resistencia a la flexión no son sustantivas; pero, si es rentable en su dosificación superplastificante, pues en la relación óptima A/C= 0.55 y dosificación 1.42% al adicionar 7.47kg de aditivo se ahorra 2 bolsas de cemento por m3 de mezcla y la resistencia a la compresión se incrementa en 169kg/cm2, y la flexión en 7 kg/cm2, respecto al concreto patrón, confirmándose la hipótesis general. | |
dc.description.abstract | This thesis investigated the influence of the multifunctional additive Sikament 290 N on the physical and mechanical properties of cement-sand concrete with compressive strength between 245 kg/cm2 and 385 kg/cm2, made with sand with a fineness modulus of 1.98, Type I Portland cement brand Cemento Amazónico Type GU; with water-cement ratios of 0.45, 0.55, and 0.65. This is a quantitative research study of a descriptive-explanatory nature, with a quasi-experimental design, involving 693 test specimens between standard and experimental concrete, with 99 corresponding to standard concrete (72 for compression and 27 for flexural strength) and 594 to experimental concrete (432 for compression and 162 for flexural strength). The samples for the experiment, in Sikament 290 N plasticizer dosage, were obtained by adding dosages of 0.3%, 0.5%, and 0.7% to the standard concrete, and in superplasticizer dosage by adding 0.71%, 1.06%, and 1.42%. Compressive strength was evaluated at 3, 7, and 28 days, and flexural strength was evaluated at 28 days of curing. The addition of Sikament 290 N, in the dosage range of plasticizer and superplasticizer, does influence the fresh state properties of slump, entrapped air, and unit weight; and, in the hardened state, compressive strength and flexural strength; although, in its dosage to act as a plasticizer, it is not cost-effective, given that at the optimal C/W ratio of 0.65 and a dosage of 0.5%, an additional 0.01 bags of cement and 6.46 kg of additive would be used per m³ of mixture, and the improvement in compressive strength and flexural strength is not substantial. However, it is cost-effective at its superplasticizer dosage, since at the optimal A/C ratio of 0.55 and dosage of 1.42%, adding 7.47 kg of additive saves 2 bags of cement per m3 of mixture and compressive strength increases by 169 kg/cm2, and flexural strength by 7 kg/cm2, compared to the standard concrete, confirming the general hypothesis. | En_us |
dc.description.uri | Tesis | es_ES |
dc.format | application/pdf | es_ES |
dc.identifier.uri | http://hdl.handle.net/20.500.14503/3410 | |
dc.language.iso | es | |
dc.publisher | Universidad Científica del Perú | |
dc.publisher.country | PE | es_ES |
dc.rights | info:eu-repo/semantics/openAccess | es_ES |
dc.rights.uri | http://creativecommons.org/licenses/by-nc-nd/3.0/us/ | * |
dc.subject | Concreto cemento-arena | |
dc.subject | Aditivo Sikament 290 N | |
dc.subject | Propiedades físicas | |
dc.subject | Propiedades mecánicas | |
dc.subject | Cement-sand concrete | En_us |
dc.subject | Sikament 290 N additive | En_us |
dc.subject | Physical properties | En_us |
dc.subject | Mechanical properties | En_us |
dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.01.00 | es_ES |
dc.title | Influencia del aditivo polifuncional sikament 290 n, en las propiedades en estado fresco y endurecido del concreto cemento – arena, Iquitos – 2024 | |
dc.type | Thesis | |
renati.advisor.dni | 10190397 | es_ES |
renati.advisor.orcid | https://orcid.org/0009-0007-6168-7415 | es_ES |
renati.author.dni | 77340905 | es_ES |
renati.author.dni | 42317611 | es_ES |
renati.discipline | 732267 | es_ES |
renati.juror | Cabanillas Oliva, Erlin Guillermo | es_ES |
renati.juror | Wong Ramírez, Félix | es_ES |
renati.juror | Barrera Villacorta, Benjamín Beltrán | es_ES |
renati.level | http://purl.org/pe-repo/renati/level#tituloProfesional | es_ES |
renati.type | https://purl.org/pe-repo/renati/type#tesis | es_ES |
thesis.degree.discipline | Ciencias e Ingeniería | es_ES |
thesis.degree.grantor | Universidad Científica del Perú. Facultad de Ciencias e Ingeniería | es_ES |
thesis.degree.name | Ingeniero Civil | es_ES |
Files
Original bundle
1 - 2 of 2
No Thumbnail Available
- Name:
- Ramírez Enciso, Blanca Flor y Ríos García, Willi – TESIS – Ciencias e Ingeniería.pdf
- Size:
- 7.21 MB
- Format:
- Adobe Portable Document Format
No Thumbnail Available
- Name:
- Ficha de Autorizacion - Blanca y Willi.pdf
- Size:
- 1.5 MB
- Format:
- Adobe Portable Document Format
License bundle
1 - 1 of 1
No Thumbnail Available
- Name:
- license.txt
- Size:
- 1.71 KB
- Format:
- Item-specific license agreed upon to submission
- Description: